Steel Shot

Manufacture Test Certificate Date 25.06.2024 Standard Reference Report For Report Type Chemical & Physical Sample From GAPL Sample Description S-550 HV HRC Standrad Spec. Hardness 445 44.7 >40-51HRC/400-500HV Density 7.51 cc/g >7 g/cc Microstucture Tempred Martensite Tempred Martensite Mess Size Weight (g) Retention % Standard Spec. 2.00 mm All Pass 0 All Pass 1.40 mm 460.1 92.02 85% 1.18 mm 34.6 6.92 12% Pan 0.5 0.1 3% 495.2 99.04 Chemical Analysis %wt Standrad Spec. Carbon 0.88 0.80-1.20% Silicon 0.62 40% Min Manganese 0.90 0.35-1.20% Sulphur 0.048 0.05% (Max) Phosphorus 0.050 0.05% (Max) Note :- Hardness Testing Done With 1Kgf Load Above .710mm Sizes ; 1kgf Below .710mm Sizes

Manufacture Test Certificate Date 25.06.2024 Standard Reference Report For Report Type Chemical & Physical Sample From GAPL Sample Description S-460 HV HRC Standrad Spec. Hardness 451 45.4 >40-51HRC/400-500HV Density 7.54 cc/g >7 g/cc Microstucture Tempred Martensite Tempred Martensite Mess Size Weight (g) Retention % Standard Spec. 2.00 mm All Pass 0 All Pass 1.70 mm 8.1 1.62 5% 1.18 mm 444.4 88.88 80% 1.00 mm 39.1 7.82 11% Pan 0.9 0.18 4% 492.5 98.5 Chemical Analysis %wt Standrad Spec. Carbon 0.88 0.80-1.20% Silicon 0.62 40% Min Manganese 0.90 0.35-1.20% Sulphur 0.048 0.05% (Max) Phosphorus 0.050 0.05% (Max) Note :- Hardness Testing Done With 1Kgf Load Above .710mm Sizes ; 1kgf Below .710mm Sizes

Manufacture Test Certificate Date 25.06.2024 Standard Reference Report For Report Type Chemical & Physical Sample From GAPL Sample Description S-660 HV HRC Standrad Spec. Hardness 460 46.1 >40-51HRC/400-500HV Density 7.54 cc/g >7 g/cc Microstucture Tempred Martensite Tempred Martensite Mess Size Weight (g) Retention % Standard Spec. 2.36 mm All Pass 0 All Pass 1.70 mm 485.1 97.02 85% 1.40 mm 12.3 2.46 12% Pan 0.2 0.04 3% 497.6 99.52 Chemical Analysis %wt Standrad Spec. Carbon 0.88 0.80-1.20% Silicon 0.62 40% Min Manganese 0.90 0.35-1.20% Sulphur 0.048 0.05% (Max) Phosphorus 0.050 0.05% (Max) Note :- Hardness Testing Done With 1Kgf Load Above .710mm Sizes ; 1kgf Below .710mm Sizes Report Prepared by Report Apporved by Signature Signature

Manufacture Test Certificate Date 25.06.2024 Standard Reference Report For Report Type Chemical & Physical Sample From GAPL Sample Description S-170 HV HRC Standrad Spec. Hardness 444 44.8 >40-51HRC/400-500HV Density 7.50 cc/g >7 g/cc Microstucture Tempred Martensite Tempred Martensite Mesh size Weight (g) Retention % Standrad Spec. .850 mm All Pass 0 All Pass .710 mm 30.1 7.02 10% .425 mm 440.9 88.18 75% .300 mm 21.3 5.00 12% Pan 2.1 0.42 3% 494.4 98.88 Chemical Analysis %wt Standrad Spec. Carbon 0.88 0.80-1.20% Silicon 0.62 40% Min Manganese 0.90 0.35-1.20% Sulphur 0.048 0.05% (Max) Phosphorus 0.050 0.05% (Max) Note :- Hardness Testing Done With 1Kgf Load Above .710mm Sizes ; 1kgf Below .710mm Sizes

Manufacture Test Certificate Date 28.02.2024 Standard Reference Report For Report Type Chemical & Physical Sample From GAPL Sample Description S-780 HV HRC Standrad Spec. Hardness 465 46.5 >40-51HRC/400-500HV Density 7.49 cc/g >7 g/cc Microstucture Tempred Martensite Tempred Martensite Mess Size Weight (g) Retention % Standard Spec. 2.80 mm All Pass 0 All Pass 2.00 mm 465.1 93.02 85% 1.70 mm 30.1 6.02 12% Pan 0.1 0.02 3% 495.3 99.06 Chemical Analysis %wt Standrad Spec. Carbon 0.88 0.80-1.20% Silicon 0.62 40% Min Manganese 0.90 0.35-1.20% Sulphur 0.048 0.05% (Max) Phosphorus 0.050 0.05% (Max) Note :- Hardness Testing Done With 1Kgf Load Above .710mm Sizes ; 1kgf Below .710mm Sizes

Manufacture Test Certificate Date 28.02.2024 Standard Reference Report For Report Type Chemical & Physical Sample From GAPL Sample Description S-390 HV HRC Standrad Spec. Hardness 469 46.9 >40-51HRC/400-500HV Density 7.54 cc/g >7 g/cc Microstucture Tempred Martensite Tempred Martensite Mess Size Weight (g) Retention % Standard Spec. 1.70 mm All Pass 0 All Pass 1.40 mm 5.5 1.1 5% 1.00 mm 456 91.2 80% .850 mm 30.1 6.02 11% Pan 1.1 0.22 4% 492.7 98.54 Chemical Analysis %wt Standrad Spec. Carbon 0.88 0.80-1.20% Silicon 0.62 40% Min Manganese 0.90 0.35-1.20% Sulphur 0.048 0.05% (Max) Phosphorus 0.050 0.05% (Max) Note :- Hardness Testing Done With 1Kgf Load Above .710mm Sizes ; 1kgf Below .710mm Sizes

Manufacture Test Certificate Date 28.02.2024 Standard Reference Report For Report Type Chemical & Physical Sample From GAPL Sample Description S-110 HV HRC Standrad Spec. Hardness 430 43.6 >40-51HRC/400-500HV Density 7.51 cc/g >7 g/cc Microstucture Tempred Martensite Tempred Martensite Mesh size Weight (g) Retention % Standrad Spec. .600 mm All Pass 0 All Pass .425 mm 46.2 9.24 10% .300 mm 445.6 89.12 75% Pan 2.1 0.42 3% 493.9 98.78 Chemical Analysis %wt Standrad Spec. Carbon 0.88 0.80-1.20% Silicon 0.62 40% Min Manganese 0.90 0.35-1.20% Sulphur 0.048 0.05% (Max) Phosphorus 0.050 0.05% (Max) Note :- Hardness Testing Done With 1Kgf Load Above .710mm Sizes ; 1kgf Below .710mm Sizes